40% talc-filled PP-Homopolymercompound, low emission and low odour
POLYFORT FPP 40T LE K2274 GRY61465
Description
Availability
Africa-Middle East, Asia-Pacific, Europe, Latin America, North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Volume Flow Rate (230 °C/2.16 kg) | 8.0 cm³/10 min |
| Density (Method A) | 1.25 g/cm³ |
| Tensile Modulus (1 mm/min, Type 1A) | 4000 MPa |
| Tensile Stress at Break (Type 1A, 5 mm/min) | 30.0 MPa |
| Tensile Strain at Break (Type 1A, 5 mm/min) | 3.5 % |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 2.5 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A) | 1.8 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) | 20 kJ/m² |
| Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise) | 11 kJ/m² |
| Vicat Softening Temperature (A (10N), 50 °C/h) | 155 °C |
| Vicat Softening Temperature (B (50N), 50 °C/h) | 90.0 °C |
| Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise) | 130 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise) | 90.0 °C |
| Burning Rate (2.00 mm) | 48 mm/min |
| Burning Rate (2.00 mm) | 48 mm/min |
| Drying Time | 2.0 to 3.0 hr |
| Drying Temperature | 80 °C |
| Processing (Melt) Temp | 220 to 260 °C |
| Mold Temperature | 30 to 60 °C |
| Flame Rating (1.5 mm) | HB |
| Flame Rating (3.0 mm) | HB |
| Flammability Classification (1.5 mm) | HB |
| Flammability Classification (3.0 mm) | HB |
Technical Data Sheet
Technical Data Sheet - APS InjectionProcess
Injection Molding
Resin
Polypropylene, Homopolymer