ASA 485CS 50591 UVGRY

LyondellBasell

Description

Centrex ASA 485CS 50591 UVGRY is a Acrylonitrile Styrene Acrylate material and is typically used in Coextrusion, Extrusion, Thermoforming applications. Features include: Good Melt Strength, Good Weather Resistance, Low Gloss, Medium Impact Resistance, and UV Resistant.

Availability

North America

Legend

SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Melt Flow Rate (220 °C/10.0 kg) 6.1 g/10 min
Melt Flow Rate (220 °C/10.0 kg) 5.0 g/10 min
Density (23 °C, Method A) 1.07 g/cm³
Density - Specific Gravity 1.06 g/cm³
Tensile Strength at Yield (5.1 mm/min) 26.5 MPa
Flexural Modulus (1.3 mm/min, Tangent) 1380 MPa
Tensile Modulus (5.1 mm/min) 1450 MPa
Flexural Strength (1.3 mm/min) 38.6 MPa
Instrumented Dart Impact (23 °C, Total Energy) 24.0 J
Instrumented Dart Impact (-30 °C, Total Energy) 6.00 J
Instrumented Dart Impact (-18 °C, Total Energy) 16.0 J
Notched Izod Impact (-40 °C, 3.18 mm) 43 J/m
Notched Izod Impact (23 °C, 3.18 mm) 130 J/m
Notched Izod Impact (-18 °C, 3.18 mm) 64 J/m
Rockwell Hardness (R-Scale) 69
Vicat Softening Temperature 100 °C
Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm) 68.3 °C
Coefficent of Linear Thermal Expansion (CLTE), Flow 9.4E-05 cm/cm/°C
Gloss (60°) 20
Gloss (60°) 10
Drying Time 3.0 to 4.0 hr
Melt Temperature 204 to 243 °C
Suggested Max Moisture <0.030 %
Die Temperature 210 to 241 °C
Suggested Max Regrind 40 %
Drying Temperature 82 to 93 °C
Flame Rating (1.5 mm) HB
UL File Number (USA) E150937

Process

Coextrusion, Extrusion


Resin

Acrylonitrile Styrene Acrylate


Applications

Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, Exterior Trim, Outdoor Applications