ALC - 2080BKBLK

LyondellBasell

Description

Alcryn 2080BK INJ BLK is a Melt Processable Rubber material and is typically used in Blow Molding, Extrusion, Injection Molding, Vacuum Forming applications. Features include: Fast Molding Cycle, Good Weather Resistance, High Flow, High Heat Resistance, Noise Damping, Oil Resistant, Ozone Resistant, Recyclable Material, and Vibration Damping.

Availability

Asia-Pacific, Europe, North America

Legend

SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Density 1.17 g/cm³
Density - Specific Gravity 1.17 g/cm³
Change in Volume (in Reference Fuel B, 27 °C, 168 hr) 32 %
Change in Volume (in Reference Fuel B, 27 °C, 168 hr) 32 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr) -8.0 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr) -8.0 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr) 31 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr) 31 %
Change in Volume (in Water, 100 °C, 168 hr) 5.0 %
Change in Volume (in Water, 100 °C, 168 hr) 5.0 %
Melt Viscosity (190 °C, 300 sec^-1) 700 Pa·s
Tensile Stress at 100% (1.90 mm) 6.20 MPa
Tensile Stress at 100% (1.90 mm) 6.20 MPa
Tensile Stress at 100% (125 °C, 1.90 mm) 5.20 MPa
Tensile Stress at 100% (125 °C, 1.90 mm) 5.20 MPa
Torsion Modulus (24 °C, 1.9 mm) 3.2 MPa
Torsion Modulus (-20 °C, 1.9 mm) 27.5 MPa
Tensile Set 10 %
Clash-Berg Modulus (-17 °C) 68.9 MPa
Tensile Strength at Yield (1.90 mm) 12.1 MPa
Tensile Strength at Yield (125 °C, 1.90 mm) 11.0 MPa
Tensile Stress at Yield (1.90 mm) 12.1 MPa
Tensile Stress at Yield (125 °C, 1.90 mm) 11.0 MPa
Tensile Strain at Break (1.90 mm) 320 %
Tensile Strain at Break (125 °C, 1.90 mm) 240 %
Tensile Elongation at Break (125 °C, 1.90 mm) 240 %
Tensile Elongation at Break (1.90 mm) 320 %
Tear Strength (Die C, 1.90 mm) 35.0 kN/m
Ductile/Brittle Transition Temperature -86 °C
Ductile/Brittle Transition Temperature -86 °C
Change in Shore Hardness in Air (Shore A, 125 °C, 168 hr) -2.0
Shore Hardness (Shore A, 1.90 mm, Compression Molded) 78
Change in Durometer Hardness in Air (Shore A, 125 °C, 168 hr) -2.0
Durometer Hardness (Shore A, 1.90 mm, Compression Molded) 78
Compression Set (24 °C, 22 hr, Method B) 14 %
Compression Set (100 °C, 22 hr, Method B) 62 %
Compression Set (24 °C, 22 hr) 14 %
Compression Set (100 °C, 22 hr) 62 %
Taber Abrasion Resistance (CS-17 Wheel, 1000 g, 1000 Cycles) 3.00 mg
Processing (Melt) Temp 177 °C
UL File Number (USA) E51193

Process

Blow Molding, Extrusion, Injection Molding, Vacuum Forming


Resin

Melt Processable Rubber


Applications

Cable Jacketing, Coating Applications, Fabric Coatings, Flexible Grips, Gaskets, General Purpose, Handles, Hose, Overmolding, Profiles, Seals, Tubing, Weatherstripping, Wire & Cable